The steel used in AV Series towers has been galvanized with a heavy zinc 
coating averaging 2.0 mils in thickness. AV Series towers are also available 
in stainless steel, which is even more corrosion resistant than galvanized 
steel in certain environments. Other materials used (PVC fill, drift eliminators, 
and louvers, aluminum fans, etc.) are selected to offer maximum service 
life in a “normal” cooling tower environment, defined as follows:

Circulating water with a pH between 6.5 and 8; a chloride content (as NaCl) 
below 500 ppm; a sulfate content (SO4) below 250 ppm; total alkalinity 
(as CaCO

3

) below 500 ppm; calcium hardness (as CaCO

3

) above 50 ppm; 

a  maximum  inlet  water  temperature  not  to  exceed  125°F  (51.7°C);  no 
significant contamination with unusual chemicals or foreign substances; 
and adequate water treatment to minimize scaling.

•  Startup Conditions: The water conditions during the initial tower opera-

tion are crucial in preventing premature corrosion of galvanized steel 
(white rust). For at least the first eight weeks of operation, pH should 
be controlled between 6.5 and 8.0 with hardness and alkalinity levels 
between 100 and 300 ppm (expressed as CaCO

3

).

•  Chlorine (if used) shall be added intermittently, with a free residual not 

to  exceed  1  ppm—maintained  for  short  periods.  Excessive  chlorine 
levels may deteriorate sealants and other materials of construction.

•  An atmosphere surrounding the tower no worse than “moderate indus-

trial”, where rainfall and fog are no more than slightly acid, and they do 
not contain significant chlorides or hydrogen sulfide (H

2

S).

•  Many proprietary chemicals exist for control of scale, corrosion, and 

biological growth and should be used prudently. Also, combinations 
of chemicals may cause reactions which reduce treatment effective-
ness, and certain chemicals such as surfactants, biodispersants and 
antifoams may increase drift rate.