ABSplus is a true production-grade thermoplastic that is durable enough to perform virtually the same as production parts. When 
combined with Design Series 3D Printers, ABSplus is ideal for building 3D models and prototypes in an office environment.

Heat Deflection (HDT) @ 66 psi

ASTM D648

204°F

96°C

Heat Deflection (HDT) @ 264 psi

ASTM D648

180°F

82°C

Glass Transition Temperature (Tg)

DSC (SSYS)

226°F

108°C

Melt Point

- - - - - - - - -

Not Applicable

3

Not Applicable

3

Coefficient of Thermal Expansion

ASTM E831

4.90E-05 in/in/°F

8.82E-05 mm/mm/°C

Volume Resistivity

ASTM D257

2.6E15 - 5.0E16 ohm-cm

Dielectric Constant

ASTM D150-98 

2.3 - 2.85

Dissipation Factor

ASTM D150-98 

0.0046 - 0.0053

Dielectric Strength

ASTM D149-09, Method A, XZ Orientation

130 V/mil

Dielectric Strength

ASTM D149-09, Method A, ZX Orientation

290 V/mil

Production-Grade Thermoplastic  

for Design Series 3D Printers

Flexural Strength (Method 1, 0.05”/min)

ASTM D790

8,450 psi

5,050 psi

58 MPa

35 MPa

Flexural Modulus (Method 1, 0.05”/min)

ASTM D790

300,000 psi

240,000 psi

2,100 MPa

1,650 MPa

Flexural Strain at Break (Method 1, 0.05”/min)

ASTM D790

4%

4%

2%

2%

Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min)

ASTM D638

4,700 psi

33 MPa

Tensile Strength, Yield (Type 1, 0.125”, 0.2”/min)

ASTM D638

450 psi

8 MPa

Tensile Modulus (Type 1, 0.125”, 0.2”/min)

ASTM D638

320,000 psi

2,200 MPa

Tensile Elongation at Break (Type 1, 0.125”, 0.2”/min)

ASTM D638

6% 

6% 

Tensile Elongation at Yield (Type 1, 0.125”, 0.2”/min)

ASTM D638

2%

2%

IZOD Impact, notched (Method A, 23°C)

ASTM D256

2.0 ft-lb/in

106 J/m