Contact  the  local  water  heater  supplier  or  service  agency  for 

further  information  concerning  an Anode  replacement  Kit  and 

this chlorination treatment.
If hot water odor persists after anode replacement and chlorination 

treatment, we can only suggest that chlorination or aeration of 

the water supply be considered to eliminate the water problem.
Do not remove the anode leaving the tank unprotected. by doing 

so, all warranty on the water heater tank is voided.
“air” in hot water fauCets

HYDrOGen  GAS:  Hydrogen  gas  can  be  produced  in  a  hot 

water system that has not been used for a long period of time 

(generally  two  weeks  or  more).  Hydrogen  gas  is  extremely 

flammable and explosive. To prevent the possibility of injury 

under  these  conditions,  we  recommend  that  the  hot  water 

faucet located farthest away from the water heater be opened 

for  several  minutes  before  any  electrical  appliances  which 

are connected to the hot water system are used (such as a 

dishwasher or washing machine). If hydrogen gas is present, 

there will probably be an unusual sound similar to air escaping 

through  the  pipe  as  the  hot  water  faucet  is  opened.  There 

must be no smoking or open flame near the faucet at the time 

it is open.

This water heater is equipped with a manual reset type high 

limit  (energy  Cutout)  switch.  The  high  limit  switch  interrupts 

the  main  burner  gas  flow  should  water  temperature  reach 

203°F (95°C).
In  the  event  of  high  limit  switch  operation,  the  water  heater 

cannot be restarted unless the water temperature is reduced to 

approximately 120°F (49°C). The high limit reset button on the 

front of the thermostat then needs to be depressed. See Figure 2 

for the location of the reset button.

It is not uncommon to experience a small amount of smoke and 

odor during the initial start-up. This is due to burning off of oil 

from metal parts, and will disappear in a short while.

Possible noises due to expansion and contraction of some metal 

parts during periods of heat-up and cool-down do not necessarily 

represent harmful or dangerous conditions.
Condensation causes sizzling and popping within the burner area 

during  heating  and  cooling  periods  and  should  be  considered 

normal.

In  each  water  heater  there  is  installed  at  least  one  anode  rod 

for  corrosion  protection  of  the  tank.  Certain  water  conditions 

will cause a reaction between this rod and the water. The most 

common  complaint  associated  with  the  anode  rod  is  one  of  a 

“rotten egg smell” in the hot water. The smell is a result of four 

factors which must all be present for the odor to develop:
a.  A concentration of sulfate in the supply water.
b.  little or no dissolved oxygen in the water.
c.  A sulfate reducing bacteria which has accumulated within the 

water heater (this harmless bacteria is nontoxic to humans).

d.  An excess of active hydrogen in the tank. This is caused by 

the corrosion protective action of the anode.

Hot  water  odor  may  be  eliminated  or  reduced  in  some  water 

heater models by replacing the anode(s) with one of less active 

material,  and  then  chlorinating  the  water  heater  tank  and  all 

water lines.