FUJIFILM PRODUCT INFORMATION BULLETIN • FUJICOLOR PRO 160 NS PROFESSIONAL
- 6 -
15. TECHNOLOGIES INCORPORATED IN
FUJICOLOR PRO 160 NS PROFESIONAL
15-1 Super Nano-Structured Σ Grain Technology
Super Nano-Structured ∑ Grain Technology provides
nano-scale control over silver halide crystals, enhancing
the efficiency at which photoelectrons are gathered
into the sensitivity nuclei during exposure. The result is
finer grain and higher speeds. Through this technology,
FUJICOLOR PRO 160 NS PROFESSIONAL is able to
boast better grain quality, higher sharpness and more
smoothly continuous tones than the current NPS, even
with the same film speed.
Super Nano-Structured ∑ Grain Technology provides
nano-scale control over silver halide crystals, enhancing
the efficiency at which photoelectrons are gathered
into the sensitivity nuclei during exposure. The result is
finer grain and higher speeds. Through this technology,
FUJICOLOR PRO 160 NS PROFESSIONAL is able to
boast better grain quality, higher sharpness and more
smoothly continuous tones than the current NPS, even
with the same film speed.
15-2 Super Efficient DIR Coupler Technology
Super Efficient DIR Coupler Technology has enabled
the free control of the interlayer effect, resulting in even
better color reproduction than that of the current film, as
well as an edge-effect-enhanced sharpness.
Super Efficient DIR Coupler Technology has enabled
the free control of the interlayer effect, resulting in even
better color reproduction than that of the current film, as
well as an edge-effect-enhanced sharpness.
15-3 Super Efficient Coupler Technology
Through the incorporation of new, high-color-generation
yellow couplers, this film has realized thinner layers and
higher sharpness.
Through the incorporation of new, high-color-generation
yellow couplers, this film has realized thinner layers and
higher sharpness.
15-4 Super Efficient Light Control Technology
The cutting of unnecessary reflected light by a new
light-absorbing agent has enabled this film to enjoy
suppressed color blurring and increased sharpness.
The cutting of unnecessary reflected light by a new
light-absorbing agent has enabled this film to enjoy
suppressed color blurring and increased sharpness.
16.
FILM STRUCTURE
17. DIFFUSE RMS GRANULARITY VALUE
····
3
*
Micro-Densitometer Measurement Aperture
: 48 μm in diameter
Sample Density: +1.0 above minimum density
* Based on Fujifilm measurements. Due to difference in
measurement conditions, comparison with color reversal film is
not possible.
18.
RESOLVING POWER
Test-Object Contrast: 1.6:1 ............
63 lines/mm
Test-Object Contrast: 1000:1 ........
125 lines/mm