12.4  Annealing 

The blade must now be annealed, or cooled at a 
controlled rate to prevent it becoming too brittle. 

The general procedure follows. Specific procedure 
will depend upon blade type, as described in 
sections 12.4.1  through 12.4.3. 

1.  Turn pressure selector knob all the way to left 

so clamp jaws are closest to each other. 

2.  Insert blade into clamps so that weld area is 

centered between clamps. Secure blade in 
jaws with the clamp handles. 

3.  Quickly press and release (“jog”) the anneal 

button (Figure 13). Repeat jog process until 
you see a slightly red glow from weld area. 

  Do not press and hold the 

4.  Release both blade clamps, allow blade to 

cool, then remove blade from clamps. 

5.  Check weld integrity. Bend blade to form a 

radius at point of weld. The size of the radius 
should be approximately the same as radius of 
band saw drive wheel. The weld must hold and 
not break or crack after forming the radius. If 
the weld breaks, cut away welded area and 
repeat welding-annealing process. 

6.  Check to make sure welded section is same 

thickness as rest of blade. If not, grind off 

excess weld material using the grinder. Refer 
to section 12.5, Blade grinding.  

  If blade is thicker at the weld 

12.4.1  Carbon steel blades 

1.  Press and jog the annealing switch button until 

weld is a "dull cherry" to "cherry red" color. 

2.  Allow blade to cool slowly by decreasing 

jogging frequency. 

12.4.2  Carbon steel hard back blades 

1.  Heat blade slowly until weld becomes a deep 

blue color. 

2.  Continue to heat by jogging the anneal button 

until the width of the blue color is one-half the 
length of the band exposed between the jaws. 

3.  Do not overheat or the temper of the band will 

be damaged.  Caution - Do not heat beyond 
the "blue" stage.  If the band begins to show 
any red color, it is too hot.  Cool quickly by 
releasing the anneal button. 

 

12.4.3  Bi-Metal blades 

1.  Heat blade slowly by jogging the annealing 

switch button until weld just begins to emit light 
(dull red color). The desired color may not 
always be visible in normal room light - always 
shade the weld area with your hand. 

2.  Cool the weld quickly by releasing the 

annealing button. 

3.  Follow this procedure before and after grinding 

bimetal blades.