multicoat slatexabover Benutzerhandbuch

The MULTICOAT SLATEX ABOVE GRADE SYS-

TEM is a multi-layer protective coating designed

for decks 200 sq. ft. or less.  For decks larger

than 200 sq. ft., please refer to the SLATEX SYS-

TEM re-inforced with 2.5 galvanized metal lath. 

This system combines an elastomeric water-

proofing membrane (MULASTICOAT) with a

fiberglass re-inforced, synthetic resin modified

cementitious top coating (KRETE KOTE 2000 or

TOP COAT 2000).

The SLATEX ABOVE GRADE SYSTEM is

designed to withstand heavy foot traffic on

decks, ramps, walkways, etc.  The SLATEX

ABOVE GRADE SYSTEM can be applied to

concrete, wood, magnesite and most other sur-

faces or substrates in need of a waterproofing

and/or fire resistant protective coating.

l

Low Cost - Minimum Down Time - Easy 

to Apply

l

Superior Waterproofing

l

Hard, Durable, Anti-Skid Surface

l

Maintains Surface Integrity Over Minor

Substrate Movement

l

Excellent Weather-Salt-Fire Resistance

l

Superior Bonding to Substrate

l

Excellent Freeze-Thaw Resistance

l

High Impact and Abrasion Resistance

l

Waterbase - Environmentally Safe to Use

and Apply

SEE TEST DATA

All substrates, concrete or wood, must be
structurally sound, free from all grease, oil,
paint, dirt, dust, sealers, curing compounds,
and other foreign materials which may 
prevent proper bonding. Substrates should be
constructed in compliance with all applicable
building codes.

Plywood substrates, including tongue and
groove plywood, must be 5/8” minimum thick-
ness, exterior grade CC PTS plywood, 16”
maximum support spacing, edges blocked,
all fastened with 8 penny ring shank nails or
equivalent, on maximum 6” centers. (NOTE:
Plywood must be nailed on all four sides.)

Moisture content should be below 15%. Use
moisture meter to check. DO NOT USE OVER
O.S.B. BOARD OR MARINE GRADE PLY-
WOOD. NOTE: All above grade decks should
be properly vented.

CONCRETE SUBSTRATE  Open cracks with a
crack chaser to 1/4" and clean out dust and
residue. Cracks and all holes, voids, etc.,
must be filled with suitable filling material. See
“CRACK REPAIR SYSTEM” and “MULTI-
PATCH SYSTEM”for details.

SLA

TEX

SY

STE

M

(Ab

ove

Gra

de)

FLASH ALL EDGES AND CAULK PLYWOOD JOINTS

POLY FAB EMBEDDED IN

MULASTICOAT OVER JOINTS/FLASHING. TWO

COATS MULASTICOAT OVER ENTIRE SURFACE.

ROLL OR TROWEL DOWN FIRST COAT OF 

AND EMBED FIBERGLASS MESH.

- SECOND COAT - TROWELED

COVER FIBERGLASS COMPLETELY.

APPLY TEXTURE COAT AND 

.