Техническая Спецификация для Emmerich Li-ion battery ICR-18650 NQ-SP 3.7 V 2600 mAh (Ø x H) 18.4 mm x 70 mm 233974

 

Spec. No. 

ICR18650-26F 

Version No. 

0.0 

 

 

 

 

4 

0.05C cut-off and the discharge (discharge current 1500mA) with 2.75V cut-off. 

Capacity after 299cycles and plus 1 day, measured under the same condition   

            in 7.2 
                                    Capacity 

≥   1785mAh(70% of the capacity at 25℃) 

 
 
    7.9 Storage Characteristics 
            Capacity after storage for 30days at 25

℃  from the standard charge,   

            measured with discharge current 1300mA with 2.75V cut-off at 25

℃. 

 

Capacity retention(after the storage) 

≥   2040mAh (80% of the capacity at 25℃) 

 

7.10 Status of the cell as of ex-factory 

            The cell should be shipped in 50% charged state. In this case, OCV is from 3.65V to   

3.85V. 

 
8. Mechanical Characteristics 
 
    8.1 Drop Test 

Test method: Cell(as of shipment or full charged) drop onto the oak-board 

(thickness: 

≥ 30mm) from 1.5m height at a random direction 6 times. 

            Criteria: No leakage 

   

8.2 Vibration Test 

            Test method: Cell(as of shipment) is vibrated along 2 mutually 
                                    perpendicular axes with total excursion of 1.6mm and with   
                                    frequency cycling between 10Hz and 55Hz by 1Hz/min. 

Criteria: No leakage 
 

9. Safety 
 
    9.1 Overcharge Test 
            Test method: To charge the standard charged cell with 12V and 2.6A at 25

℃   

                                    for 2.5 hours. 
            Criteria: No fire, and no explosion. 
 
    9.2 External Short-circuit Test 
            Test method: To short-circuit the standard charged cell by connecting positive and   
                                    negative terminal by less than 50m

Ω   wire for 3hours. 

            Criteria: No fire, and no explosion. 
 
    9.3 Reverse Charge Test 

Test method: To charge the standard charged cell with charge current 2.6A   

By –12V for 2.5 hours.   

            Criteria: No fire, and no explosion. 
 

9.4 Heating Test